Dye-incorporated composition

ABSTRACT

A dye-incorporated composition which comprises a cyanine type dye and an azo metal chelate compound comprising an azo type compound of the following formula (I): ##STR1## (wherein A is a residue forming a hetero ring together with the carbon atom and the nitrogen atom to which it is bonded, B is a residue forming an aromatic ring or a hetero ring together with the two carbon atoms to which it is bonded, and X is a group having an active hydrogen), and a metal, and an optical recording medium comprising a recording layer which contains the dye-incorporated composition.

TECHNICAL FIELD

The present invention relates to a dye-incorporated compositioncomprising a cyanine type dye and an azo metal chelate compound, and anoptical recording medium using it, more particularly, to adye-incorporated composition which shows an absorption within the rangeof from 600 to 800 nm and has excellent light fastness and moistureresistance, useful for various optical recording media,electro-photosensitive materials, color liquid crystal displaymaterials, light beam cut filters or the like, and an optical recordingmedium using it.

BACKGROUND ART

An optical recording medium employing laser makes storage andreproduction of high density information records possible, and itsdevelopment have been remarkable recent years.

As an example of the optical recording medium, an optical disc may bementioned. In general, an optical disc is usually designed to irradiatea focused laser beam of about 1 μm, to a thin recording layer formed ona substrate of disc shape to conduct high density information recording.The recording is carried out in such a manner that upon absorption ofthe layer beam energy, the irradiated portion of the recording layerwill undergo a thermal deformation such as decomposition, evaporation ormelting. Reproduction of the recorded information is carried out byreading the difference in the reflectance between the portion having adeformation formed by the laser beam and the portion having no suchdeformation.

Accordingly, an optical recording medium is required to efficientlyabsorb the energy of the laser beam, and also required to have apredetermined amount of absorbed light to a laser beam having a specificwavelength employed for recording and to be high in the reflectance to alaser beam having a specific wavelength employed for reproduction foraccurately conducting the reproduction of information.

As the optical recording medium of this kind, there have been proposedones comprising an organic dye thin film formed on a substrate. Since itis possible to form the organic dye thin film by coating, its massproductivity is high and the cost is expected to be low.

It has been known that a thin film containing the cyanine type dye isemployed as the organic dye thin film (reference can be made withJapanese Unexamined Patent Publications No. 112790/1983, No.114989/1983, No. 85791/1984 and No. 83236/1985). However, the opticalrecording medium comprising such a cyanine type dye is poor in the lightstability, and has a problem in the storage stability and a drawbacksuch that it is prone to light deteriorating upon reproduction. Thus,Japanese Unexamined Patent Publications No. 55795/1984, NO. 40389/1989,No. 55189/1990, No. 68742/1990, etc. propose to add various metalchelate compounds represented by the following structural formula (1),(2), (3) or (4), to the cyanine type dye to improve the light stability.However, the improvement is still on an insufficient level. ##STR2##

DISCLOSURE OF THE INVENTION

The present invention relates to a dye-incorporated composition whichcomprises a cyanine type dye and a metal chelate compound comprising anazo type compound of the following formula (I): ##STR3## (wherein A is aresidue forming a hetero ring together with the carbon atom and thenitrogen atom to which it is bonded, B is a residue forming an aromaticring or a hetero ring together with the two carbon atoms to which it isbonded, and X is a group having an active hydrogen), and a metal, and anoptical recording medium using it.

Namely, an object of the-present invention is to provide adye-incorporated composition containing a cyanine type dye and an azometal chelate compound, which is excellent in the light fastness andmoisture resistance as a dye for various chemical information materialssuch as optical recording media, and suitable to spin coating, and toprovide an optical recording medium, which has the composition in itsrecording layer, being excellent in the light stability and causing nolight deterioration upon reproduction.

Now, the present invention will be described in detail.

In the azo type compound of the formula (I), A is a residue forming anitrogen-containing hetero ring together with the carbon atom and thenitrogen atom to which it is bonded, and the hetero ring is specificallya thiazole ring, a benzothiazole ring, a pyridobenzothiazole ring, abenzopyridothiazole ring, a pyridothiazole ring, a pyridine ring, aquinoline ring or the like. These nitrogen-containing hetero rings mayhave a substituent such as an alkyl group, an alkoxy group, an aryloxygroup, an aralkyl group, an aryl group, a halogen atom, a cyano group, anitro group, an ester group, a carbamoyl group, an acyl group, anacylamino group, a sulfamoyl group, a sulfonamide group, an amino group,a hydroxyl group, a phenylazo group, a pyridinoazo group or a vinylgroup. These substituents may further have a substituent. Among thesubstituents of the nitrogen-containing hereto rings, preferred is aC₁₋₂₅ alkyl group which may have a substituent, a C₁₋₂₅ alkoxy groupwhich may have a substituent, a halogen atom, a cyano group, a nitrogroup, a C₁₋₂₅ alkylsulfamoyl group which may have a substituent, aC₆₋₃₀ phenylsulfamoyl group which may have a substituent, a phenylazogroup which may have a substituent, a pyridinoazo group which may have asubstituent, a C₂₋₂₆ ester group, a C₂₋₂₆ carbamoyl group, a C₂₋₂₆ acylgroup, a C₁₋₂₅ acylamino group, a C₁₋₂₅ sulfonamide group, --NR⁹ R¹⁰ (R⁹and R¹⁰ which are independent from each other, is a hydrogen atom, aC₁₋₂₅ alkyl group which may have a substituent or a phenyl group whichmay have a substituent, and R⁹ and R¹⁰ may form a 5-membered ring or a6-membered ring each together), a hydroxyl group, --CR¹¹ ═C(CN)R¹² (R¹¹is a hydrogen atom or a C₁₋₆ alkyl group and R¹² is a cyano group or aC₂₋₇ alkoxycarbonyl group) or the like.

In the azo type compound of the formula (I), B is a residue forming anaromatic ring or a hereto ring together with the two carbon atoms towhich it is bonded, and is specifically a benzene ring, a naphthalenering, a pyridine ring, a pyridone ring, a tetrahydroquinoline ring, apyrazole ring or the like. The aromatic rings or the hetero rings mayhave a substituent, and such a substituent is an alkyl group, an alkoxygroup, an aryloxy group, an aralkyl group, an aryl group, a halogenatom, a cyano group, a nitro group, an ester group, a carbamoyl group,an acyl group, an acylamino group, a sulfamoyl group, a sulfonamidegroup, an amino group, a hydroxyl group, a phenylazo group, apyridinoazo group, a vinyl group or the like. These substituents mayfurther have a substituent. Among the substituents on these aromaticrings or hetero rings, preferred is a C₁₋₂₅ alkyl group which may have asubstituent, a C₁₋₂₅ alkoxy group which may have a substituent, ahalogen atom, a cyano group, a nitro group, a C₁₋₂₅ alkylsulfamoyl groupwhich may have a substituent, a C₆₋₃₀ phenylsulfamoyl group which mayhave a substituent, a phenylazo group which may have a substituent, apyridinoazo group which may have a substituent, a C₂₋₂₆ ester group, aC₂₋₂₆ carbamoyl group, a C₂₋₂₆ acyl group, a C₁₋₂₅ acylamino group, aC₁₋₂₅ sulfonamide group, --NR⁹ R¹⁰ (each of R⁹ and R¹⁰ which areindependent from each other, is a hydrogen atom, a C₁₋₂₅ alkyl groupwhich may have a substituent or a phenyl group which may have asubstituent, and R⁹ and R¹⁰ may form a 5-membered ring or a 6-memberedring each together ), a hydroxyl group, --CR¹¹ ═C(CN)R¹² (R¹¹ is ahydrogen atom or a C₁₋₆ alkyl group and R¹² is a cyano group or a C₂₋₇alkoxycarbonyl group) or the like.

In the azo type compound of the formula (I), X is not particularlylimited so far as it is a group having an active hydrogen, butpreferably --OH, --COOH, --SO₃ H--, --B(OH)₂, --HNSO₂ R¹³ (R¹³ is ahydrogen atom, a C₁₋₂₅ alkyl group which may have a substituent or aphenyl group which may have a substituent), --CONH₂, --SO₂ NH₂, --NH₂ orthe like. Particularly preferred are --OH, --COOH, --SO₃ H, --HNSO₂ R¹³(R¹³ is as defined above). In the instance where X is a group whichdissociates in anions such as --COOH, --OH, --SO₃ H, etc., in theformation of the azo metal chelate compound, the azo type compound maybe used as such, but may be used in the form of a salt with a cation. Assuch a cation, inorganic cations such as Na⁺, Li⁺, K⁺ or the like andorganic type cations such as ##STR4## the like may be mentioned. Amongthe azo type compounds of the formula (I), preferred is an azo typecompound of the following formula (III ): ##STR5## (wherein R⁷ and R⁸which are independent from each other, is a hydrogen atom, an alkylgroup which may have a substituent, an aryl group which may have asubstituent, an alkenyl group which may have a substituent or acycloalkyl group which may have a substituent, A and X are as definedabove, and the ring D may have a substituent). Among the azo typecompounds of the formula (III), particularly preferred is an azo typecompound of the formula (IV): ##STR6## (wherein X' is a hydrogen atom ora cation, and R⁷ R⁸, A and ring D are as defined above):

As the substituents which may be substituted for the alkyl group, thearyl group, the alkenyl group or the cycloalkyl group which arerepresented by R⁷ and R⁸ in the formulas (III ) and ( IV), for example,an alkoxy group, an alkoxyalkyl group, an alkoxyalkoxyalkoxy group, anallyloxy group, an aryl group, an aryloxy group, a cyano group, a nitrogroup, a hydroxy group, a tetrahydrofuryl group, an alkylsulfonylaminogroup, a halogen atom and the like may be mentioned. In addition, as thesubstituents for the aryl group and cycloalkyl group, an alkyl group ora vinyl group may be mentioned. As the substituents which may besubstituted for the ring D, an alkyl group, an alkoxy group, a halogenatom and the like may be mentioned.

Among the azo type compounds of the formula (I), another type of apreferred compound is an azo type compound of the following formula (V):##STR7## (wherein Y is a residue forming an aromatic ring or a heretoring together with the thiazole ring to which it is bonded, and B and Xare as defined above). Among the azo type compounds of the formula(III), particularly preferred is an azo type compound of the followingformula (VI): ##STR8## (wherein X' is a hydrogen atom or a cation, and R7 R⁸, Y, ring D and X' are as defined above).

In the formulas (V) and (VI), Y is a residue forming an aromatic ring ora hetero ring together with the thiazole ring to which it is bonded,specifically a benzene ring, a naphthalene ring, an anthracene ring, aphenanthrene ring, a pyridine ring, a quinoline ring, a thiophene ring,a carbazole ring, a fluorene ring, an anthraquinone ring or the like.Such a residue Y may have thereon the same substituents as defined forthe above A.

As the metals forming the chelate compounds together with the azo typecompounds, there is no particular limitation so far as these are metalshaving an ability of forming the chelate compounds with the azo typecompounds, but preferred are transition elements such as nickel (Ni)cobalt (Co), iron, ruthenium, rodium, palladium, copper, osmium, iridiumor platinum, and particularly preferred are Ni and Co. These are used inthe form of a salt such as Ni(CH₄ COO)₂, NiCl₂, CoCl₂, Co(BF₄)₂ orCo(CH₃ COO)₂ for the preparation, and obtained as a complex in whichNi²⁺, Co²⁺, Co³⁺ or the like is coordinated.

The metal chelate compound of the azo compound employed in the presentinvention can be obtained according to the description of, for example,Furukawa; Analytica Chemica Acta 140 (1982) 281-289. For example, themetal chelate compound of the azo type compound of the formula (III) canbe obtained by diazotizing an amino compound of the formula (VII):##STR9## (wherein A is as defined above) according to the ordinarymethods, conducting a coupling with a substituted anilinesulfonatederivative of the following formula (VIII): ##STR10## (wherein ring D,R⁷, R⁸ and X are as defined above) to obtain an azo type compound of theformula (III), and then reacting said azo type compound with a metalsalt in water and/or an organic solvent such as dioxane,tetrahydrofuran, acetone or ethanol to obtain the metal chelate compoundof the present invention.

As an anion of the metal salt to be used for the preparation of themetal chelate compound, preferred is a monovalent or divalent anion suchas SCN⁻, SbF₆ ⁻, Cl⁻, Br⁻, F⁻, ClO₄ ⁻, BF₄ ⁻, PF₆ ⁻, CH₃ COO⁻, TiF₆ ²⁻,SiF₆ ²⁻, ZrF₆ ²⁻, ##STR11## Particularly preferred is BF₄ ⁻, PF₆ ⁻ orCH₃ COO⁻.

As preferred specific examples of the chelate compound of the azo typecompound and the metal employed for the dye-incorporated composition ofthe present invention, the azo metal chelate compounds as shown in thefollowing Tables 1 to 9 may be mentioned.

                                      TABLE 1                                     __________________________________________________________________________     ##STR12##                                                                    Compound No.                                                                          R.sup.7                                                                            R.sup.8                                                                            R.sup.13   R.sup.14                                                                          R.sup.15                                                                          R.sup.16                                                                           W    M   L     n  m                 __________________________________________________________________________    1       C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    CH.sub.3   H   H   H    SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2  --                2       C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    CH.sub.3   CH.sub.3                                                                          H   H    SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2  --                3       C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    CH.sub.3   H   H   OCH.sub.3                                                                          SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2  --                4       C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                     ##STR13## H   H   H    SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2  --                5       C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                     ##STR14## H   H   H    SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2  --                6       CH.sub.3                                                                           CH.sub.3                                                                           CH.sub.3   H   H   H    COO.sup.-                                                                          Ni.sup.2+                                                                         --    2  --                7       C.sub.3 H.sub.7(n)                                                                 C.sub.3 H.sub.7(n)                                                                 CH.sub.3   H   H   H    COO.sup.-                                                                          Cu.sup.2+                                                                         --    2  --                8       C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    CH.sub.3   H   H   H    COO.sup.-                                                                          Co.sup.3+                                                                         Cl.sup.-                                                                            2  1                 9       C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    OCH.sub.3  H   H   H    COO.sup.-                                                                          Co.sup.3+                                                                         BF.sub.4 .sup.-                                                                     2  1                 10      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    CH.sub.3   H   H   H    SO.sub.3.sup.-                                                                     Co.sup.3+                                                                         CH.sub.3 COO.sup.-                                                                  2  1                 11      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    Br         H   H   H    COO.sup.-                                                                          Cu.sup.2+                                                                         --    2  --                12      CH.sub.3                                                                           CH.sub.3                                                                           OC.sub.2 H.sub.5                                                                         H   H   CH.sub.3                                                                           SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2  --                __________________________________________________________________________

                                      TABLE 2                                     __________________________________________________________________________     ##STR15##                                                                    Compound No.                                                                          R.sup.7                                                                            R.sup.8                                                                            R.sup.16                                                                           W    M   L     n m                                     __________________________________________________________________________    13      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    H    SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2 --                                    14      C.sub.2 H.sub.5                                                                    C.sub.4 H.sub.9(n)                                                                 H    SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2 --                                    15      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    OCH.sub.3                                                                          SO.sub.3.sup.-                                                                     Ni.sup.2+                                                                         --    2 --                                    16      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    H    SO.sub.3.sup.-                                                                     Co.sup.3+                                                                         CH.sub.3 COO.sup.-                                                                  2 1                                     __________________________________________________________________________

                                      TABLE 3                                     __________________________________________________________________________     ##STR16##                                                                    Compound No.                                                                          R.sup.7                                                                            R.sup.8                                                                            R.sup.16                                                                         R.sup.19                                                                         R.sup.20                                                                         W    M   L     n m                                 __________________________________________________________________________    17      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    H  Br Br O.sup.-                                                                            Ni.sup.2+                                                                         --    2 --                                18      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    H  Cl H  O.sup.-                                                                            Co.sup.3+                                                                         Cl.sup.-                                                                            2 1                                 19      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    H  Cl H  O.sup.-                                                                            Ni.sup.2+                                                                         --    2 --                                20      C.sub.3 H.sub. 7(n)                                                                C.sub.3 H.sub.7(n)                                                                 H  Br Br COO.sup.-                                                                          Co.sup.2+                                                                         --    2 --                                21      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    H  Cl H  O.sup.-                                                                            Co.sup.3+                                                                         BF.sub.4.sup.-                                                                      2 1                                 22      C.sub.3 H.sub.7(n)                                                                 C.sub.3 H.sub.7(n)                                                                 H  Br Br COO.sup.-                                                                          Co.sup.3+                                                                         CH.sub.3 COO.sup.-                                                                  2 1                                 23      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    H  Br Br SO.sup.3-                                                                          Co.sup.3+                                                                         Cl.sup.-                                                                            2 1                                 __________________________________________________________________________

                                      TABLE 4                                     __________________________________________________________________________     ##STR17##                                                                    Compound No.                                                                          R.sup.7                                                                            R.sup.8                                                                            R.sup.17                                                                          R.sup.18   R.sup.16                                                                         W    M  L n m                             __________________________________________________________________________    24      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    CH.sub.3                                                                          H          H  COO.sup.-                                                                          Ni.sup.2+                                                                        --                                                                              2 --                            25      C.sub.2 H.sub.5                                                                    C.sub.2 H.sub.5                                                                    CH.sub.3                                                                           ##STR18## H  SO.sub.3 .sup.-                                                                    Ni.sup.2+                                                                        --                                                                              2 --                            __________________________________________________________________________

                  TABLE 5                                                         ______________________________________                                        Formula                                                                        ##STR19##                                                                    M(L).sub.m                                                                    Com-                                                                          pound                                                                         No.   R.sup.7  R.sup.8  R.sup.16                                                                           W      M    L   n   m                            ______________________________________                                        26    C.sub.2 H.sub.5                                                                        C.sub.2 H.sub.5                                                                        H    COO.sup.-                                                                            Ni.sup.2+                                                                          --  2   --                           27    C.sub.2 H.sub.5                                                                        C.sub.2 H.sub.5                                                                        H    SO.sub.3 .sup.-                                                                      Ni.sup.2+                                                                          --  2   --                           ______________________________________                                    

                  TABLE 6                                                         ______________________________________                                        Formula                                                                        ##STR20##                                                                    M(L).sub.m                                                                    Com-                                                                          pound                                                                         No.   R.sup.7  R.sup.8  R.sup.16                                                                           W      M    L   n   m                            ______________________________________                                        28    C.sub.2 H.sub.5                                                                        C.sub.2 H.sub.5                                                                        H    SO.sub.3 .sup.-                                                                      Ni.sup.2+                                                                          --  2   --                           29    C.sub.2 H.sub.5                                                                        C.sub.2 H.sub.5                                                                        H    SO.sub.3 .sup.-                                                                      Co.sup.2+                                                                          --  2   --                           ______________________________________                                    

                                      TABLE 7                                     __________________________________________________________________________     ##STR21##                                                                    Compound No.                                                                          E            R.sup.21                                                                           M   L  n m                                          __________________________________________________________________________    30                                                                                     ##STR22##   C.sub.2 H.sub.5                                                                    Ni.sup.2+                                                                         -- 2 --                                         31                                                                                     ##STR23##   C.sub.3 H.sub.7(n)                                                                 Co.sup.3+                                                                         Cl.sup.-                                                                         2 1                                          __________________________________________________________________________

                                      TABLE 8                                     __________________________________________________________________________     ##STR24##                                                                    Compound No.                                                                          E            R.sup.22                                                                          R.sup.23                                                                              M   L   n m                                  __________________________________________________________________________    32                                                                                     ##STR25##   CH.sub.3                                                                          H       Ni.sup.2+                                                                         --  2 --                                 33                                                                                     ##STR26##   CH.sub.3                                                                          SO.sub.2 NHC.sub.2 H.sub.5                                                            Co.sup.3+                                                                         PF.sub.6 .sup.-                                                                   2 1                                  __________________________________________________________________________

                                      TABLE 9                                     __________________________________________________________________________     ##STR27##                                                                    Compound No.                                                                          E            R.sup.24                                                                              M   L  n m                                       __________________________________________________________________________    34                                                                                     ##STR28##   SO.sub.2 NHC.sub.2 H.sub.5                                                            Ni.sup.2+                                                                         -- 2 --                                      35                                                                                     ##STR29##   SO.sub.2 NHC.sub.2 H.sub.5                                                            Co.sup.3+                                                                         Cl.sup.-                                                                         2 1                                       __________________________________________________________________________

As the cyanine type dye, any conventional ones may be employed, butparticularly preferred is an indolenine type cyanine dye of thefollowing formula (II): ##STR30## (wherein P and P' which areindependent from each other, is a residue forming an aromatic ringtogether with the two carbon atoms to which it is bonded, Q is apentamethine group which may have a substituent, each of R¹, R², R³, R⁴,R⁵ and R⁶ which are independent from each other, is an alkyl group whichmay-have a substituent, an aryl group which may have a substituent, analkenyl group which may have a substituent or a cycloalkyl group whichmay have a substituent, and Z⁻ is an anionic residue). Such indoleninetype cyanine dyes can be easily synthesized by a method described in,for example, Japanese Unexamined Patent Publications No. 112790/1983,114989/1983, No. 85791/1984, No. 83236/1985 or the like.

The dye-incorporated composition of the present invention is comprisedof the cyanine type dye and the metal chelate compound formulated at theratio of 5:95 to 99:1, preferably 5:95 to 50:50 by weight.

The dye-incorporated composition of the present invention shows anabsorption within the range of 600 to 800 nm and is excellent in thelight fastness and the moisture resistance.

The dye-incorporated composition of the present invention can beemployed for, for example, a recording layer of an optical recordingmedium. The optical recording medium usually produced is basicallycomposed of a substrate and a recording layer containing a cyanine typedye and a metal chelate compound of an azo type compound, but, ifnecessary, a reflecting layer may be provided on the recording layer.Further, if necessary, a primer coating layer may be provided on thesubstrate, a protecting layer may be provided on the recording layer orthe reflecting layer, and a surface protecting layer may be provided onthe substrate at the opposite side to the recording layer (mirrorsurface side).

In the present invention, the substrate is preferably transparent to thelaser beam to be employed. With respect to the material for thesubstrate, a support commonly used for recording material such as glassor plastic may be employed. From various aspects, plastic material ispreferably used. As such plastic material, acryl resin, methacryl resin,vinyl acetate resin, vinyl chloride resin, nitro cellulose, polyethyleneresin, polypropylene resin, polycarbonate resin, polyimide resin, epoxyresin or polysulfone resin may be mentioned.

Among them, an injection molded polycarbonate resin substrate isparticularly preferably employed from the viewpoint of the highproductivity, low cost and moisture resistance.

As the reflective layer, employed are metals such as gold, silver,copper, aluminum or platinum and alloys thereof which have highreflectance in the laser wavelength region to be employed.

As the protective layer, an ultraviolet curable acryl resin or a silicontype hard coating agent is employed.

As the surface protective layer on the mirror surface side of thesubstrate, an ultraviolet curable acryl resin or a silicon type hardcoating agent is employed. The surface protecting layer is preferablyprovided with an antistatic' ability for preventing dust or the likefrom adhering.

The recording layer of the present invention containing the cyanine typedye and the metal chelate of the azo type compound has a film thicknessof usually from 100 Å to 5 μm, preferably from 700 Å to 2 μm.

With respect to the layer-forming method, the layer may be formed by acommonly employed thin film-forming method such as a vacuum vapordeposition method, a sputtering method, a doctor blade method, a castingmethod, a spinner method or a dipping method. However, the spinnermethod is preferred from the viewpoint of the productivity and cost.

In the case of layer forming by a spinner method, the rotational speedis preferably from 500 to 5,000 rpm, and after spin coating, treatmentsuch as heating or exposing to a solvent vapor, can be applied, as thecase requires.

Further, a binder may be used as the case requires. As such a binder, aknown binder such as polyivinyl alcohol, polyvinylpyrrolidone,nitrocellulose, cellulose acetate, ketone resin, polyvinylbutyral orpolycarbonate, may be employed.

When a recording layer is formed by a coating method such as a doctorblade method, a casting method, a spinner method or a dipping method,particularly a spinner method, as the coating solvent, the one having aboiling point of from 120 to 160° C., such as tetrafluoropropanol,octafluoropentanol, tetrachloroethane, bromoform, dibromoethane,diacetone alcohol, ethyl cellosolve, xylene,3-hydroxy-3-methyl-2-butanone, chlorobenzene, cyclohexanone or methyllactate, is preferably employed.

Among them, for the injection molded polycarbonate resin substrateexcellent in the high productivity, low cost and moisture resistance, asa solvent suitably useful without damaging the substrate, a ketonealcohol type solvent such as diacetone alcohol or3-hydroxy-3-methyl-2-butanone; a cellosolve type solvent such as methylcellosolve or ethyl cellosolve; a perfluoroalkyl alcohol type solventsuch as tetrafluoropropanol or octafluoropentanol; or a hydroxyestertype solvent such as methyl lactate or methyl isobutylate, may bementioned.

The recording layer of the optical recording medium of the presentinvention may be formed on both sides of the substrate or on one sidethereof.

Recording on an optical recording medium thus obtained, is conducted byirradiating a laser beam, preferably a semiconductor laser beam, focusedto about 1 m to the recording layer provided on both sides of thesubstrate or on one side thereof. At the portion irradiated with thelaser beam, a thermal deformation of the recording layer, such asdecomposition, evaluation or melting, will be formed due to absorptionof the laser energy.

Reproduction of the recorded information can be conducted by reading thedifference in the reflectance between the portion having such a thermaldeformation formed by a laser beam and the portion having no such athermal deformation.

As the laser beam to be used for the optical recording medium of thepresent invention, N₂, He--Cd, At, H₃ --Ne, ruby, a semiconductor or adye laser, may be mentioned. However, a semiconductor laser is usedparticularly preferably from the viewpoint of light weight, conveniencein handling and compactness.

BEST MODE FOR CARRYING OUT THE INVENTION

Now, the present invention will be described in detail with reference toexamples. However, the present invention is by no means restricted tosuchExamples unless it exceeds its gist.

EXAMPLE 1

A mixture (weight ratio 70:30) of 0.28 g of an indolenine type cyaninedye of the following structural formula: ##STR31##and 0.12 g of an azometal chelate compound of the following structural formula (Compound No.1 of the above Table 1): ##STR32##was dissolved in 40 g ofoctafluoropentanol to obtain a 1 wt % solution. This solution wasdropped on an injection molded polycarbonate substrate having a diameterof 120 mm, a thickness of 1.2 mm, and a groove with a depth of 1,000 Åand a width of 0.7 μm, and coated thereon by a spinner method (arotational speed of 500 rpm for 4 minutes). The coating was followed bydrying at 80° C. for 5 minutes to form a recording layer.

Then, on the recording layer, a gold layer having a layer thickness of2,000 Å was formed by a sputtering method as a reflecting layer.Further, on this reflecting layer, an ultraviolet curable resin wasspin-coated, followed by irradiation with ultraviolet rays for curing toform a protecting layer having a thickness of 10 μm, to obtain anoptical recording medium.

EFM modulating signals were recorded on the obtained optical recordingmedium with a semiconductor laser beam having a wavelength of 785 nm ata linear velocity of 1.4 m/s, and then reproduced. From the reproducedwave shape, a reflectance and a degree of lit modulation were measured.The degree of lit modulation represented by percentage, is a valueobtained bydividing the signal amplitude of the longest recording pit bythe reflectance.

Further, photo-deterioration accelerated test (test conditions; JISstandard L0843-1988, temperature 63±3° C., apparatus used for the test;Xenon Long Life Weather Meter manufactured by Suga Shikenki)wasconducted by continuously irradiating a xenon light having an outputof 2.5kW with a distance of 25 cm, and then the reflectance and thedegree of litmodulation were measured.

Further, a track on which EFM signals were recorded, was repeatedlyreproduced 500,000 times with a laser beam having an output of 1.2 mW,andthe reflectance and the degree of lit modulation were measured. Theresultsare shown in Table 10.

EXAMPLE 2

An optical recording medium was obtained in the same manner as inExample 1except that a dye of the following structural formula:##STR33##as an indolenine type cyanine dye, and a compound of thefollowing structural formula (Compound No. 6 of Table 1): ##STR34##as anazo metal chelate compound were mixed at a weight ratio of 70:3 andused.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 3

An optical recording medium was obtained in the same manner as inExample 1except that a dye of the following structural formula:##STR35##as an indolenine type cyanine dye, and a compound of thefollowing structural formula (Compound No. 5 of Table 1): ##STR36##as anazo metal chelate compound were mixed at a weight ratio of 70:30 andused.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 4

An optical recording medium was obtained in the same manner as inExample 1except that a dye of the following structural formula:##STR37##as an indolenine type cyanine dye, and a compound (Compound No.13 of Table2) of the following structural formula: ##STR38##as an azometal chelate compound were mixed at a weight ratio of 60:40 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 5

An optical recording medium was obtained in the same manner as inExample 1except that a dye of the following structural formula:##STR39##as an indolenine type cyanine dye, and a compound (Compound No.19 of Table3) of the following structural formula: ##STR40##as an azometal chelate compound were mixed at a weight ratio of 80:20 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 6

An optical recording medium was obtained in the same manner as inExample 1except that a dye of the following structural formula:##STR41##as an indolenine type cyanine dye, and a compound (Compound No.21 of Table3) of the following structural formula: ##STR42##as an azometal chelate compound were mixed at a weight ratio of 80:20 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 7

An optical recording medium was obtained in the same manner as inExample 1except that a dye of the following structural formula:##STR43##as an indolenine type cyanine dye, and a compound (Compound No.22 of Table3) of the following structural formula: ##STR44##as an azometal chelate compound were mixed at a weight ratio of 70:30 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 8

An optical recording medium was obtained in the same manner as inExample 1except that a dye of the following structural formula:##STR45##as an indolenine type cyanine dye, and a compound (Compound No.30 of Table7) of the following structural formula: ##STR46##as an azometal chelate compound were mixed at a weight ratio of 80:20 and used.

The reflectance and the degree of lit modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 9

An optical recording medium was obtained in the same manner as inExample 1except that 26 g of methyl lactate was used instead of 40 g ofoctafluoropentanol as a coating solvent.

The reflectance and the degree of lit modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

EXAMPLE 10

An optical recording medium was obtained in the same manner as inExample 1except that 23 g of 3-hydroxy-3-methyl-2-butanone was usedinstead of 40 g of octafluoropentanol as a coating solvent.

The reflectance and the degree of lit modulation were measured in thesame manner as in Example 1, and the results are shown in Table 10.

COMPARATIVE EXAMPLE 1

An optical recording medium was produced in the same manner as inExample 1except that a recording layer was formed by using only theindolenine type cyanine dye without using the azo metal chelatecompound. The reflectance and the degree of lit modulation were measuredin the same manner as in Example 1, and the results are shown in Table10.

COMPARATIVE EXAMPLE 2

An optical recording medium was produced in the same manner as inExample 3except that a recording layer was formed by using only theindolenine type cyanine dye without using the azo metal chelatecompound. The reflectance and the degree of lit modulation were measuredin the same manner as in Example 1, and the results are shown in Table10.

COMPARATIVE EXAMPLE 3

An optical recording medium was produced in the same manner as inExample 5except that a recording layer was formed by using only theindolenine type cyanine dye without using the azo metal chelatecompound. The reflectance and the degree of lit modulation were measuredin the same manner as in Example 1, and the results are shown in Table10.

COMPARATIVE EXAMPLE 4

An optical recording medium was produced in the same manner as inExample 1except that the indolenine type cyanine dye used in Example 1and a metal chelate compound of the following structural formula:##STR47##were mixed at a weight ratio of 70:30 and used. The reflectanceand the degree of lit modulation were measured in the same manner as inExample 1,and the results are shown in Table 10.

                  TABLE 10                                                        ______________________________________                                                       After        After repeated                                    Initial value  accelerated test                                                                           reproduction                                                Degree           Degree       Degree                                          of               of           of                                    Reflec-   modula-  Reflec- modula-                                                                              Reflec-                                                                             modula-                               tance     tion     tance   tion   tance tion                                  (%)       (%)      (%)     (%)    (%)   (%)                                   ______________________________________                                        Ex-   71      70       78    66     76    68                                  ample                                                                         Ex-   69      67       74    62     73    65                                  ample                                                                         2                                                                             Ex-   65      67       75    63     73    65                                  ample                                                                         3                                                                             Ex-   70      69       78    66     73    67                                  ample                                                                         4                                                                             Ex-   67      63       76    61     74    62                                  ample                                                                         5                                                                             Ex-   66      64       75    60     71    61                                  ample                                                                         6                                                                             Ex-   66      66       72    65     70    65                                  ample                                                                         7                                                                             Ex-   72      65       81    62     73    64                                  ample                                                                         8                                                                             Ex-   71      69       77    66     74    68                                  ample                                                                         9                                                                             Ex-   70      70       78    65     77    69                                  ample                                                                         10                                                                            Com-  75      72       88    34     84    45                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         1                                                                             Com-  74      69       86    29     83    50                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         2                                                                             Com-  76      72       90    31     85    52                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         3                                                                             Com-  73      70       87    48     82    59                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         4                                                                             ______________________________________                                    

EXAMPLE 11

A dye-incorporated composition (a weight ratio of 30:70) of 0.28 g a dyeofthe following structural formula: ##STR48##as an indolenine typecyanine dye, and 0.28 g of a compound of the following structuralformula: ##STR49##as an azo metal chelate compound, was dissolved inoctafluoropentanol to obtain a 2 wt % solution. An optical recordingmedium was obtained in the same manner as in Example 1 by using thesolution.

The reflectance and the degree of 11% modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 12

An optical recording medium was obtained in the same manner as inExample 11 except that a dye of the following structural formula:##STR50##as an indolenine type cyanine dye, and a compound (Compound No.6 of Table 1) of the following structural formula: ##STR51##as an azometal chelate compound were mixed at a weight ratio of 30:70 and used.

The reflectance and the degree of lit modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 13

An optical recording medium was obtained in the same manner as inExample 11 except that a dye of the following structural formula:##STR52##as an indolenine type cyanine dye, and a compound (Compound No.5 of Table 1) of the following structural formula: ##STR53##as an azometal chelate compound were mixed at a weight ratio of 30:70 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 14

An optical recording medium was obtained in the same manner as inExample 11 except that a dye of the following structural formula:##STR54##as an indolenine type cyanine dye, and a compound (Compound No.13 of Table2) of the following structural formula: ##STR55##as an azometal chelate compound were mixed at a weight ratio of 40:60 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 15

An optical recording medium was obtained in the same manner as inExample 11 except that a dye of the following structural formula:##STR56##as an indolenine type cyanine dye, and a compound (Compound No.19 of Table3) of the following structural formula: ##STR57##as an azometal chelate compound were mixed at a weight ratio of 20:80 and used.The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 16

An optical recording medium was obtained in the same manner as inExample 11 except that a dye of the following structural formula:##STR58##as an indolenine type cyanine dye, and a compound (Compound No.21 of Table3) of the following structural formula: ##STR59##as an azometal chelate compound were mixed at a weight ratio of 20:80 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 17

An optical recording medium was obtained in the same manner as inExample 11 except that a dye of the following structural formula:##STR60##as an indolenine type cyanine dye, and a compound (Compound No.22 of Table3) of the following structural formula: ##STR61##as an azometal chelate compound were mixed at a weight ratio of 30:70 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 18

An optical recording medium was obtained in the same manner as inExample 11 except that a dye of the following structural formula:##STR62##as an indolenine type cyanine dye, and a compound (Compound No.22 of Table3) of the following structural formula: ##STR63##as an azometal chelate compound were mixed at a weight ratio of 20:80 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 19

An optical recording medium was obtained in the same manner as inExample 11 except that 13 g of methyl lactate was employed instead of 20g of octafluoropentanol as a coating solvent.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 20

An optical recording medium was obtained in the same manner as inExample 11 except that 11.5 g of 3-hydroxy-3-methyl-2-butanone wasemployed instead of 20 g of octafluoropentanol as a coating solvent.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 21

A dye-incorporated composition (a weight ratio of 15:85) of 0.10 g of adyeof the following structural formula: ##STR64##as an indolenine typecyanine dye and 0.62 g of a compound of the followingstructural formula:##STR65##as an azo metal chelate compound was dissolved in 20 g ofoctagluoropentanol to obtain a 3.6 wt % solution. The solution wasdroppedon an injection molded polycarbonate substrate having a diameterof 120 mm and a thickness of 1.2 mm with a groove having a depth of1,900 Å and a width of 0.45 μm, and coated by a spinner method(rotational speed: 500 rpm, 4 minutes). After coating, drying wasconducted at 80° C. for 5 minutes to form a recording layer. The, areflecting layer and a protecting layer are formed on the recordinglayer in the same manner as in Example 1 to produce an optical recordingmedium.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

EXAMPLE 22

An optical recording medium was obtained in the same manner as inExample 21 except that a dye of the following structural formula:##STR66##as an indolenine type cyanine dye, and a compound of thefollowing structural formula: ##STR67##as an azo metal chelate compoundwere mixed at a weight ratio of 15:85 and used.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

COMPARATIVE EXAMPLE 5

An optical recording medium was produced in the same manner as inExample 11 except that a recording layer was formed by using only theindolenine type cyanine dye without using the azo metal chelatecompound.

The reflectance and the degree of lit modulation were measured in thesame manner as in Example 1, and the results are shown in Table 11.

COMPARATIVE EXAMPLE 6

An optical recording medium was produced in the same manner as inExample 13 except that a recording layer was formed by using only theindolenine type cyanine dye without using the azo metal chelatecompound.

The reflectance and the degree of lit modulation were measured in thesame manner as in Example 11, and the results are shown in Table 11.

COMPARATIVE EXAMPLE 7

An optical recording medium was produced in the same manner as inExample 15 except that a recording layer was formed by using only theindolenine type cyanine dye without using the azo metal chelatecompound.

The reflectance and the degree of lit modulation were measured in thesame manner as in Example 11, and the results are shown in Table 11.

COMPARATIVE EXAMPLE 8

An optical recording medium was produced in the same manner as inExample 11 except that the indolenine type cyanine dye used in Example11 and a metal chelate compound of the following structural formula:.##STR68##were mixed at a weight ratio of 70:30.

The reflectance and the degree of 11T modulation were measured in thesame manner as in Example 11, and the results are shown in Table 11.

                  TABLE 11                                                        ______________________________________                                                       After        After repeated                                    Initial value  accelerated test                                                                           reproduction                                                Degree           Degree       Degree                                          of               of           of                                    Reflec-   modula-  Reflec- modula-                                                                              Reflec-                                                                             modula-                               tance     tion     tance   tion   tance tion                                  (%)       (%)      (%)     (%)    (%)   (%)                                   ______________________________________                                        Ex-   74      72       83    68     79    69                                  ample                                                                         11                                                                            Ex-   69      68       81    63     76    65                                  ample                                                                         12                                                                            Ex-   68      67       80    62     75    63                                  ample                                                                         13                                                                            Ex-   75      70       83    66     79    67                                  ample                                                                         14                                                                            Ex-   66      65       76    62     74    64                                  ample                                                                         15                                                                            Ex-   66      65       77    63     74    64                                  ample                                                                         16                                                                            Ex-   67      66       74    64     71    65                                  ample                                                                         17                                                                            Ex-   71      65       80    61     73    64                                  ample                                                                         18                                                                            Ex-   74      71       82    67     78    68                                  ample                                                                         19                                                                            Ex-   73      69       82    65     79    67                                  ample                                                                         20                                                                            Ex-   71      80       76    78     73    79                                  ample                                                                         21                                                                            Ex-   69      82       73    77     71    81                                  ample                                                                         22                                                                            Com-  77      75       89    18     84    27                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         Com-  77      72       88    18     86    29                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         6                                                                             Com-  78      74       91    19     86    32                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         7                                                                             Com-  75      69       88    41     82    52                                  para-                                                                         tive                                                                          Ex-                                                                           ample                                                                         8                                                                             ______________________________________                                    

EFFECTS OF THE INVENTION

Since the dye-incorporated composition of the present inventioncomprising an indolenine type cyanine dye and a metal chelate compound,shows absorption in the range of 600 to 800 nm and is excellent in thelight fastness and the moisture resistance, it can be advantageouslyused for various optical recording media, electro-photosensitivematerials, color liquid crystal display materials, light beam cutfilters or the like. Further, an optical recording medium of the presentinvention using the dye-incorporated composition, is excellent in lightstability and causes no light deterioration during reproduction, suchbeing useful.

We claim:
 1. A dye-incorporated composition which comprises a mixture ofa cyanine dye and an azo metal chelate compound, wherein the azo metalchelate compound is an azo compound of the following formula (I):##STR69## wherein A is a residue forming a hetero ring together with thecarbon atom and the nitrogen atom to which it is bonded, B is a residueforming an aromatic ring or a hetero ring together with the two carbonatoms to which is bonded, and X is a group having an active hydrogen,wherein ##STR70## is a thiazole ring, a benzothiazole ring, apyridobenzothiazole ring, a binzopyridothiazole ring, a pyridothiazolering, a pyridine ring or a quinoline ring; or a thiazole ring, abenzothioazole ring, a pyridobenzothiazole ring, a benzopyridothiazolering, a pyridothiazole ring, a pyridine ring or a quinoline ringsubstituted by an alkyl group, an alkoxy group, an aryloxy group, anaralkyl group, an aryl group, a halogen atom, a cyano group, a nitrogroup, an ester group, a carbamoyl group, an acyl group, an aclyaminogroup, a sulfamoyl group, a sulfonamide group, an amino group a hydroxylgroup, a phenylazo group, a pyridinoazo group or a vinyl group; and##STR71## is a benzene ring, a naphthalene ring, a pyridine ring, apyridone ring, a tetrahydroquinoline ring or a pyrazole ring; or abenzene ring, a naphthalene ring, a pyridine ring, a pyridone ring, atetrahydroquinoline ring or a pyrazole ring substituted by an alkylgroup, an alkoxy group, an aryloxy group, an aralkyl group, an arylgroup, a halogen atom, a cyano group, a nitro group, an ester group, acarbamoyl group, an acyl group, an acylamino group, a sulfamoyl group, asulfonamide group, an amino group, a hydroxyl group, a phenylazo group,a pyridinoazo group or a vinyl group;chelated with a metal.
 2. Thedye-incorporated composition according to claim 1, wherein the cyaninedye is an indolenine cyanine dye of the following formula (II):##STR72## wherein each of P and P' which are independent from eachother, is a residue forming an aromatic ring together with the twocarbon atoms to which it is bonded, Q is a pentamethine which may have asubstituent, each of R³, R⁴, R⁵, R⁶, R⁷ and R⁸ which are independentfrom one another, is an alkyl group which may have a substituent, anaryl group which may have a substituent, an alkenyl group which may havea substituent, or a cycloalkyl group which may have a substituent, andz⁻ is an anion residue.
 3. The dye-incorporated composition according toclaim 1, wherein the cyanine dye and the azo metal chelate compound areprepared in the ratio of 5:95 to 95:5 by weight.
 4. The dye-incorporatedcomposition according to claim 3, wherein the azo compound is an azocompound of the following formula (III): ##STR73## wherein A is aresidue forming a hetero ring together with the carbon atom and thenitrogen atom to which it is bonded, each of R⁷ and R⁸ which areindependent from each other, is a hydrogen atom, an alkyl group whichmay have a substituent, an aryl group which may have a substituent, analkenyl group which may have a substituent or a cycloalkyl group whichmay have a substituent, X is a group having an active hydrogen; and thering D may have a substituent.
 5. The dye-incorporated compositionaccording to claim 4, wherein the azo compound is an azo compound of thefollowing formula (IV): ##STR74## wherein A is a residue forming ahetero ring together with the carbon atom and the nitrogen atom to whichit is bonded, each of R⁷ and R⁸ which are independent from each other,is a hydrogen atom, an alkyl group which may have a substituent, an arylgroup which may have a substituent, an alkenyl group which may have asubstituent or a cycloalkyl group which may have a substituent, X' is ahydrogen atom or a cation, and the ring D may have a substituent.
 6. Thedye-incorporated composition according to claim 3, wherein the azocompound is an azo compound of the following formula (V): ##STR75##wherein Y is a residue forming an aromatic ring or a hetero ringtogether with the thiazole ring to which it is bonded, B is a residueforming an aromatic ring or a hetero ring together with the two carbonatoms to which it is bonded, and X is a group having an active hydrogen.7. The dye-incorporated composition according to claim 6, wherein theazo compound is an azo compound of the following formula (VI): ##STR76##wherein Y is a residue forming an aromatic ring or a hetero ringtogether with the thiazole ring to which it is bonded, X' is a hydrogenatom or a cation, and the ring D may have a substituent.
 8. Thedye-incorporated composition according to any one of claims 4 to 7 and11, wherein the metal forming the azo metal chelate compound togetherwith the azo compound is a transition element.